20.500.12556/RUL-141626 Influence of friction riveting parameters on the dissimilar joint formation and strength Friction riveting represents a promising technology for joining similar and/or dissimilar materials of light-weight components. However, the main drawback of the technology is that it is primarily used only with special machines for friction welding that have a force control. In this study we used accessible CNC machines with a position control. A set of friction riveting experiments was performed to establish the relationship between the processing parameters, the rivet formation and its mechanical strength. During the manufacturing process, the axial force and torque were constantly measured. The fabricated joints were examined using an X-ray imaging technique, microstructural analyses, and mechanical tests. The samples were subjected to the pull-out test to analyse the joints’ strength and determine the failure mode type. In addition, a correlation between the friction riveting processing parameters, the rivet penetration depth, the rivet shape and the joint strength was established. The results depict that a higher axial force in the first production phase at the higher feeding rate increases the penetration depth, while in the second phase at lower feeding rate, an anchoring shape of a rivet forms. friction riveting 2024-T351 aluminium alloy PEI polymer X-ray imaging pull-out force torno kovičenje 2024‐T351 Al zlitina PEI polimer rentgensko slikanje digitalna radiografija izvlečna sila true false true Angleški jezik Slovenski jezik Članek v reviji 2022-10-03 09:43:49 2022-10-03 09:43:53 2022-10-04 03:54:15 0000-00-00 00:00:00 2022 0 0 12 str. iss. 19, art. 6812 Vol. 15 Sep. 2022 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 2022-09-01 620.178.4:531.4 1996-1944 10.3390/ma15196812 123842051 Klobcar_..._-_Influence_of_friction_riveting_parameters_on_the_dissimilar_joint_formation_and_strength.pdf Klobcar_..._-_Influence_of_friction_riveting_parameters_on_the_dissimilar_joint_formation_and_strength.pdf 1 3CB355927EB419EC23E553FFFECB404A 64fd6619d598929c82db2034388857a27e81c5424efb7e5fb0db38a15b17252b 92b49bf1-42f0-11ed-9c94-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=162724 https://www.mdpi.com/1996-1944/15/19/6812 1 1ca041a4-42ef-11ed-9c94-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=162723 Fakulteta za strojništvo 0 0 0