20.500.12556/RUL-138909 Termično utrujanje CGHSS litine za valje za delo v vročem diplomsko delo Thermal fatique of cast iron CGHSS for hot working rolls diploma work V okviru diplomske naloge smo na termo-mehanskem simulatorju Gleeble 1500D izvajali laboratorijske preizkuse termičnega utrujanja, pri čemer smo uporabljali vzorce iz CG HSS litine, ki se uporablja za izdelavo valjev za vroče valjanje. Mikrostrukturo vzorcev smo okarakterizirali s pomočjo elektronskih mikroskopov JEOL JSM 6500F in ThermoFisher Scientific Vacuum Quattro S. Ta je sestavljena iz matrice, evtektičnih karbidov (na osnovi Fe (ca 68 mas. %)), karbidov na osnovi najvišje vrednosti za Nb (pribl. 64 - 68 mas. %) ter V in Mo, karbidov na osnovi najvišje vrednosti za V (pribl. 31 ? 32 mas. %) ter Nb in Mo ter grafitov. Preizkuse smo izvajali pri maksimalnih testnih temperaturah 500 °C ter 650 °C, pri čemer smo testiranje ustavljali pri 250, 750, 2500 in 6000 ciklih. Dolžine razpok na preizkušancih, nastalih kot posledica generiranega temperaturnega gradienta med ohlajanjem z vodo, smo izmerili s pomočjo optičnega mikroskopa. Kvantificirali smo obstojnost proti termičnemu utrujanju CG HSS litine, t.j. z izračunom srednje dolžine vseh razpok, srednje dolžine sedmih najdaljših razpok, najdaljše razpoke, gostoto razpok ter površino pod zaključenimi razpokami. Oksidacija evtektikov, grafitnih področij ter ostalih karbidov je bistveno bolj poudarjena pri višji temperaturi, t.j. pri 650 °C, kot pri nižji temperaturi testiranja, t.j. pri 500 °C. Karbidi na osnovi najvišje vrednosti za Nb kot tudi najvišje vrednosti za V izkazujejo večjo krhkost ter večjo nagnjenost k oksidaciji. Iniciacija razpok najpogosteje nastane na mestih debelejših karbidov na površini, kjer je bilo opaziti njihovo izrazito pokanje. Rast razpok pa je pretežno povezana tako s karbidno kot tudi z grafitno potjo. For the present work, the thermal fatigue resistance of CG HSS cast iron samples, typically used in the production of hot working rollers, was tested in the laboratory on the Gleeble 1500D thermo-mechanical simulator. The microstructure of the samples was characterized using JEOL JSM 6500F and ThermoFisher Scientific Vacuum Quattro S electron microscopes. The microstructure consisted of matrix, eutectic carbides (based on Fe (ca 68 wt. %)), carbides based on the highest value for Nb (ca 64 - 68 wt. %), V and Mo, carbides based on the highest value for V (ca 31 - 32 wt. %), Nb, Mo and graphites. The tests were performed at maximum test temperatures of 500 °C and 650 °C, respectively, and interrupted at 250, 750, 2500 and 6000 cycles. The length of cracks on samples created by cooling water temperature gradient was measured with an optical microscope. The resistance to thermal fatigue of CG HSS cast iron was quntified by calculating the mean length of all cracks, the mean length of the seven longest cracks, the longest crack, the crack density, and the area under linked cracks. Oxidation of eutectics, graphite areas, and other carbides was much more pronounced at higher test temperatures, i. e., 650 °C, than at a lower test temperature, i. e., 500 °C. The carbides based on the highest Nb value, as well as the highest V values, demonstrated greater brittleness and a greater tendency to oxidation. Cracks were predominantly initiated on areas with thicker carbides where pronounced cracking was observed, while crack growth was primarily associated with the carbide and graphite pathways. termično utrujanje CG HSS litina karbidi grafiti rast razpok oksidacija thermal fatigue CG HSS cast iron carbides graphites cracks oxidation true false false [B. Zupančič] Slovenski jezik Angleški jezik Diplomsko delo/naloga 2022-08-25 09:00:03 2022-08-25 09:00:13 2022-11-14 13:29:02 0000-00-00 00:00:00 2022 0 Ljubljana 0 Ljubljana XIII, 40 f. 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 669 86984 129239555 12120.pdf 12120.pdf 1 4C24AAD891967749B4BA1AB34FF6488A 28f2a9976f874eeb2b5545fee4db1056f0e6d44273695552f3a14bc8b7160034 8b24e575-2443-11ed-92af-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=159405 Naravoslovnotehniška fakulteta 0 0 0