20.500.12556/RUL-136226 Kappa carbide precipitation in duplex Fe-Al-Mn-Ni-C low-density steel The microstructural evolution of a Fe-Mn-Al-Ni-C low-density steel was studied. The lightweight low-density steels are a promising material for the transportation industry, due to their good mechanical properties and low density. The base microstructure of the investigated steel consists of ferrite and austenite. Thermo-Calc calculations showed the formation of an ordered BCC (body-centred cubic) B2 phase below 1181 °C and kappa carbides below 864 °C. The steel was produced in a vacuum induction furnace, cast into ingots and hot forged into bars. The forged bars were solution annealed and then isothermally annealed at 350, 450, 550, 650, 750, and 850 °C. The microstructure of the as-cast state, the hot forged state, solution annealed, and isothermally annealed were investigated by optical microscopy and scanning electron microscopy. The results showed the formation of kappa carbides and the ordered B2 phase. The kappa carbides appeared in the as-cast sample and at the grain boundaries of the isothermally annealed samples. At 550 °C, the kappa carbides began to form in the austenite phase and coarsened with increasing temperature. duplex steel low-density steel precipitation kappa carbides true false true Angleški jezik Ni določen Članek v reviji 2022-04-20 13:46:33 2022-04-20 13:46:33 2022-09-15 04:13:35 0000-00-00 00:00:00 2021 0 0 11 str. iss. 10, art. 1261 Vol. 11 2021 0000-00-00 Zaloznikova Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 620.1:67.017:669.1 2073-4352 10.3390/cryst11101261 81738755 crystals-11-01261-v2.pdf crystals-11-01261-v2.pdf 1 CF5765BE7BB11A26BA86A52528B56062 4cb6c65c78eb0a800dd6aae58b035b57af99ad9d366f5335e65345675a4d211b a957fc79-c09f-11ec-8aca-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=155760 https://www.mdpi.com/2073-4352/11/10/1261 1 763d011d-c09f-11ec-8aca-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=155759 Naravoslovnotehniška fakulteta 0 0 0