20.500.12556/RUL-125829 Sinteza anizotropnih superparamagnetnih mikrodelcev železovega oksida ter študija njihove kompleksacije z ioneni Synthesis of Anisotropic Superparamagnetic Iron Oxide Microparticles and Their Complexation Study with Ionenes Magnetni nanodelci zaradi svojih lastnosti izkazujejo veliko uporabno vrednost na številnih področjih, med drugim tudi v medicini, tehniki in na področju ved o okolju. V tem okviru so posebej zanimivi superparamagnetni nanodelci železovega oksida, ki so splošno sprejeti kot varni za ljudi in okolje. Obenem jih lahko relativno enostavno pripravimo v obliki stabilne koloidne suspenzije, saj se takšni delci v odsotnosti zunanjega magnetnega polja obnašajo kot nemagnetni materiali in se posledično magnetno ne agregirajo. V magistrskem delu so predstavljeni rezultati sinteze superparamagnetnih mikrodelcev v obliki paličic (mikropalčke), ki so magnetno sestavljeni iz velikega števila majhnih nanodelcev maghemita (kemijsko γ-Fe2O3). V okviru magistrskega dela sem preučevala vplive spreminjanja pogojev sinteze na tvorbo in koloidno stabilnost anizotropnih mikrostruktur, prevlečenih s plastjo silicijevega dioksida (silika). Njihovo površino sem nato funkcionalizirala s kationskim polielektrolitom 3,3-ionen bromidom. Uspešnost sinteze mikropalčk in njihove kompleksacije z ioneni sem preverila z različnimi metodami – optično in presevno elektronsko mikroskopijo, magnetnimi meritvami z magnetometrom z vibrirajočim vzorcem, ζ-potenciometrijo, obarjalno potenciometrično titracijo in organoleptično oceno. Rezultati, ki sem jih pri tem dobila, potrjujejo uspešnost sinteze mikropalčk maghemita s superparamagnetnimi lastnostmi, prevlečenja njihove površine s siliko in kompleksacije z ioneni. Due to their properties, magnetic nanoparticles are widely used in many fields, including medicine, technology and environmental sciences. Particularly interesting are superparamagnetic iron oxide nanoparticles that are generally accepted as safe for humans and the environment. At the same time, they can be relatively easily prepared in stable colloidal suspension. Such particles behave as non-magnetic materials in absence of external magnetic field and consequently do not aggregate magnetically. This master thesis represents the results of synthesis of superparamagnetic microparticles in form of rods (microrods) which are magnetically composed of a large number of small maghemite (chemical γ-Fe2O3) nanoparticles. In the master thesis I studied the effects of changing various synthesis conditions on formation and colloidal stability of anisotropic microstructures, coated with a layer of silicon dioxide (silica). Then I functionalised their surface with 3,3-ionene bromide cationic polyelectrolyte. Synthesis and complexation process was determined with optical and transmission electronic microscopy, vibrating-sample magnetometer, ζ-potentiometry potentiometric precipitation titration and organoleptically. The results confirm the success of the synthesis of maghemite microrods with superparamagnetic properties, coating their surface with silica and complexation with ionene polyelectrolytes. superparamagnetni delci koloidna suspenzija mikropalčke maghemita ioneni superparamagnetic particles colloid maghemite microrods ionene polyelectrolytes true false false Slovenski jezik Angleški jezik Magistrsko delo/naloga 2021-04-07 15:35:00 2021-04-07 15:35:11 2022-09-05 03:52:48 0000-00-00 00:00:00 2021 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 10242 59594243 Krizaj_Nina_-_Sinteza_anizotropnih_superparamagnetnih_mikrodelcev_zelezovega_oksida_ter_studija_.pdf Krizaj_Nina_-_Sinteza_anizotropnih_superparamagnetnih_mikrodelcev_zelezovega_oksida_ter_studija_.pdf 1 B0B1A866A94FC488E88E19AD18A8C3BD b9b66f46dad6b7ba1315f51363152a326540151d83063efac9b561c715819cd3 cc882d43-a1bb-11eb-a523-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=141693 Fakulteta za kemijo in kemijsko tehnologijo 0 0 0