20.500.12556/RUL-105547 Enhanced pool-boiling heat transfer on laser-made hydrophobic/superhydrophilic polydimethylsiloxane-silica patterned surfaces This study presents the application of hydrophobic polydimethylsiloxane-silica coating used for the development of biphilic surfaces that are designed to enhance the heat transfer during boiling. Surface analyses showed that this coating exhibits a high hydrophobicity due to its hierarchical structure and the use of hydrophobic polymer. An appropriate thermal treatment leads to the oxidation of the methyl groups and a formation of silicon oxide and silicon carbide that result in a wettability transition from hydrophobic to superhydrophilic. On this basis, we manufactured hydrophobic/superhydrophilic patterns on stainless-steel foils using a pulsed Nd:YAG laser. The uniform, superhydrophilic surface exhibited a 350% larger critical heat flux (CHF) than bare stainless-steel foil. High-speed IR thermography revealed that the increased wettability reduced the bubble contact diameter, allowed a higher density of active nucleation sites, and delayed the dry-out. The biphilic surfaces with differently sized hydrophobic spots exhibited the highest heat transfer coefficients, with an up to 200% higher CHF compared to the bare stainless steel. Smaller hydrophobic spots reduced the bubble diameter and increased the nucleation frequency. However, surfaces with larger hydrophobic regions promoted boiling incipience and exhibited higher heat transfer coefficients at low heat fluxes. These results suggest that the optimal biphilic pattern could only be determined for a particular operating point. Our data provide a new insight into the complex phenomena of nucleate pool boiling on chemically and mechanically heterogeneous surfaces. pool boiling heat transfer enhancement biphilic micropattern laser-processed surface high-speed IR thermography polydimethylsiloxane-silica coating vrenje v bazenu izboljšan prenos toplote bifilne mikro strukture lasersko procesirane površine hitrotekoča IR termografija polidimetilsiloksan-silika premaz true false true Angleški jezik Slovenski jezik Članek v reviji 2018-12-05 08:58:30 2018-12-05 08:58:32 2025-02-24 10:10:10 0000-00-00 00:00:00 2015 0 0 Str. 288-297 Vol. 91 Dec. 2015 0000-00-00 PostprintKoncna Objavljeno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 536.24(045) 1359-4311 10.1016/j.applthermaleng.2015.08.026 14131227 1861910 RAZ_Zupancic_Matevz_i2015.pdf RAZ_Zupancic_Matevz_i2015.pdf 1 151A5F60947076F2BCF821368141A5FF 581b18c2680ff039c96dddfc4d62dbd1e6ecb6d4b22b00905cc07e080a9792d7 3282ac0a-a1b6-11eb-a523-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=116216 Fakulteta za strojništvo 0 0 0