20.500.12556/RUL-103834 Analiza lokalnih piezoelektričnih in feroelektričnih lastnosti tankih plasti $\rm({K_{0.5}Na_{0.5})_{0.99}Sr_{0.01}NbO_3}$ Analysis of local piezoelectric and ferroelectric properties of thin films $\rm({K_{0.5}Na_{0.5})_{0.99}Sr_{0.01}NbO_3}$ Piezoelektrične in feroelektrične materiale izkoriščamo v številnih aplikacijah, kjer se pojavi potreba po medsebojni pretvorbi mehanskih v električne signale in obratno, recimo v aktuatorjih, senzorjih, ultrazvočnih pretvornikih in shranjevalcih energije. Zadnjih nekaj desetletji smo na trgu priča prevladi piezoelektričnega materiala $\rm{Pb(Zr,Ti)O_3}$. Ta material ima odlične funkcionalne lastnosti, vendar je zaradi vsebnosti svinca okolju in človeku škodljiv. Razvoj novih piezoelektričnih materialov je torej usmerjen k piezoelektričnim materialom brez svinca. Tipični predstavnik takšnih materialov je $\rm{(K,Na)NbO_3}$. Cilj zaključnega dela je bil preučiti lokalne piezoelektrične in feroelektrične lastnosti polikristalinične tanke plasti $\rm({K_{0.5}Na_{0.5})_{0.99}Sr_{0.01}NbO_3}$. Vse eksperimente sem izvedel z mikroskopom na atomsko silo. Sprva sem določil topografijo površja vzorca, hrapavost vzorca ter lokalni piezoelektrični odziv v vertikalni smeri. Hrapavost vzorca, določena na območju velikosti 2 μm x 2 μm, je bila 3 nm, povprečna vrednost lokalnega piezoelektričnega odziva d$_{33}$ pa 42 pm/V. Nadalje sem izmeril lokalno histerezno zanko faznega premika v odvisnosti od jakosti električnega polja s katerim sem obračal polarizacijo. S tem, ko sem obračal polarizacijo v izbrani točki, sem dokazal, da je vzorec lokalno feroelektričen. Piezoelectric and ferroelectric materials are used in numerous applications, such as actuators, sensors, ultrasonic transducers and energy storage devices, where conversion between mechanical and electrical signals is needed. Over the last few decades, materials based on $\rm{Pb(Zr,Ti)O_3}$ dominate the market of piezoelectric devices. That material has excellent functional properties, but it is harmful to the environment and humans due to its high content of lead. The development of new piezoelectric materials is therefore oriented towards environmental-friendly lead-free materials, such as $\rm{(K,Na)NbO_3}$-based ones. The aim of this work was to study the local piezoelectric and ferroelectric properties of the polycrystalline $\rm({K_{0.5}Na_{0.5})_{0.99}Sr_{0.01}NbO_3}$ thin films. I have done all the experiments by atomic force microscope. At first, I determined the sample topography, surface roughness and local piezoelectric response in vertical direction. The surface roughness was 3 nm (scanned on the area of 2 μm x 2 μm). The average value of the local piezoelectric response d$_{33}$ was 42 pm/V. Further, I measured the local hysteresis loop of phase shift in dependence of electric field whom I reoriented polarization. With reorienting polarization in particular point, I proved that the sample is local ferroelectric. fizika trdne snovi mikroskop na atomsko silo piezoelektriki feroelektriki tanke plasti solid state physics atomic force microscope piezoelectrics ferroelectrics thin films true false false Slovenski jezik Angleški jezik Zaključna naloga 2018-09-27 07:45:48 2018-09-27 07:45:53 2022-08-17 03:41:50 0000-00-00 00:00:00 2018 0 0 0000-00-00 NiDoloceno NiDoloceno NiDoloceno 0000-00-00 0000-00-00 0000-00-00 92365 31714343 445.pdf 445.pdf 1 0487CFD250C677FFA423F660EE52B626 642da6345518e0046802a2afd595cce87473beb87b1efb11a9607a2de2ed30b8 ea832ced-a1b5-11eb-a523-00155dcfd717 https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=114335 Fakulteta za matematiko in fiziko 0 0 0