Zaostale napetosti v zvarih na aluminijevi zlitini 7075
Residual stresses in welded aluminium alloy 7075
Zaostale napetosti so izredno pomembne iz vidika obratovalne dobe strojnega dela, saj so prisotne v materialu tudi takrat, ko nanj ne deluje nobena zunanja obremenitev in so posledica različnih proizvodnih procesov kot je litje, varjenje, preoblikovanje, toplotne obdelave itd. Napetosti lahko v splošnem razdelimo kot tlačne in natezne. V diplomski nalogi smo merili zaostale napetosti v varih na aluminijevi zlitini 7075, zvarjeni po postopku varjenja z gnetenjem. Vzorci so bili zvarjeni z orodjem iz orodnega jekla in s parametri 950 in 750 vrt/min, ter podajanji 73, 93 in 116 mm/min. Zaostale napetosti smo merili z metodo rentgenske difrakcije (ang. X-ray difraction - XRD) na mestu varjenja in toplotno vplivnem območju (TVO). Na velikost zaostalih napetosti v največji meri vpliva delež vnesene toplote. V primerjavi z drugimi postopki varjenja ima postopek varjenja z gnetenjem manjši linijski vnos toplote in posledično lahko pričakujemo manjše vrednosti zaostalih napetosti. Ugotovili smo, da se zaradi varjenja z gnetenjem v območju zvara in TVO, pojavijo natezne zaostale napetosti, kot posledica vnosa toplote in deformacij med varjenjem z gnetenjem. Toplota in deformacije privedejo do sprememb v mehanskih lastnostih materiala. Zvari z višjimi nateznimi zaostalimi napetostmi se odražajo z višjo trdoto, ter nižjo natezno trdnostjo.
Residual stresses are extremely important in terms of the operating life of the machine part, since they are present in the material even when there is no external force and are the result of their manufacture processes such as casting, welding, forming, heat treatments, etc. Residual stresses can generally be divided as tensile or compressive. In our work we measured the residual stresses in friction stir welded aluminium alloy 7075. The samples were welded with a tool made of hot work tool steel and with parameters 950 and 750 rpm, and welding speeds 73, 93 and 116 mm / min. The residual stresses were measured using the X-ray diffraction methodology across the whole weld and heat affected zone. They were measured in longitudinal and transversal direction of the weld face. The amount of residual stresses is mostly affected by the heat input. In comparison with other welding processes, friction stir welding has a smaller linear heat input, and lower residual stresses values can be expected. We found out, that due to friction stir welding in the weld area and in the HAZ, tensile residual stresses occur. Residual stresses occur as a result of heat and deformation, during friction stir welding. Due to heat and deformation, there are changes in mechanical properties. Welds with higher tensile residual stresses have higher hardness and lower tensile strength.
Merjenje zaostalih napetosti
varjenje z gnetenjem
parametrična analiza
aluminijeva zlitina 7075
rentgenska difrakcija
Measurement of residual stresses
friction stir welding
parametric analysis
aluminium alloy 7075
X-ray diffraction
true
false
false
[R. Avsenik]
Slovenski jezik
Angleški jezik
Diplomsko delo/naloga
2018-09-25 14:08:25
2018-09-25 14:08:29
2023-10-13 08:54:15
0000-00-00 00:00:00
2018
0
0
0000-00-00
NiDoloceno
NiDoloceno
NiDoloceno
0000-00-00
0000-00-00
0000-00-00
53.08:621.791:669.715(043.2)
209659
16234779
2729.pdf
2729.pdf
1
202E9A50DFEE61E9D8AF4A1207C9AE80
4b4d842f642bfc6150587dca6ce7ad666fa3f1ac59674b4d0324308af811d12f
e640758f-a1b5-11eb-a523-00155dcfd717
https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=114261
2732.xlsx
2732.xlsx
1
3C2E3E786EFF800FDB4D42A14FA47910
7d5504384bbcf0473c6f5193039ae543b7fe826b5759ed7fb03e8c39ca5c5a04
e66e5a1e-a1b5-11eb-a523-00155dcfd717
https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=114264
2730.jpg
2730.jpg
1
ECF966E8BA7503E3DB759E4812CE33CA
faa61198246eb132af320309fab9e62bceaf88c8bfa3074ae45ca1bc4c1a5839
e64f5127-a1b5-11eb-a523-00155dcfd717
https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=114262
2731.jpg
2731.jpg
1
09AF559F527CF01B8D10ACF1EBD0FEFC
23d674a8d82854f9e45562c2ee10e9d0bb204af79102bc729ffee46a72cd1b35
e65ffe75-a1b5-11eb-a523-00155dcfd717
https://repozitorij.uni-lj.si/Dokument.php?lang=slv&id=114263
Fakulteta za strojništvo
0
0
0