TG. Pri tem je potrebno upoštevati najmanjši znani difuzijski koeficient ogljika v avstenitu. Za eksperimentalne pogoje žarjenj jekel C22, C45 in C60 so bile iz omenjene enačbe razvite poenostavljene enačbe za izračun debelin razogljičenih plasti. Primerjava med izmerjenimi in teoretično izračunanimi debelinami razogljičenja je pokazala zelo veliko ujemanje rezultatov.]]>
TG. The lowest known value of the diffusion coefficient of carbon needs to be used with this equation. Equations, that can be used for calculation of the theoretical depths of decarburization for experimental conditions used in this thesis, were created from Van-Ostrand-Dewey equation. The comparison between measured and calculated results shows high levels of matching.]]>
2018
2018-09-15 07:47:32
1060
podevtektoidna jekla, razogljičenje, oksidacija, žarjenje, dvofazno področje
hypoeutectoid steels, decarburization, oxidation, annealing, dual-phased region
mb22
Matija
Zorc
70
Aleš
Nagode
991
VisID
16
64286
COBISS_ID
3
1747807
2727.pdf
6294470
Predstavitvena datoteka
2018-09-15 07:47:34