Bimetallic CoMn$_2$O$_4$ spinel as an effective catalyst for peroxymonosulfate activation toward perfluorooctanoic acid degradation

Shi, Pengcheng (avtor), Singh, Seema (avtor), Rani, Mahima (avtor), Lavrenčič Štangar, Urška (avtor), Kumar, Praveen (avtor)

The widespread occurrence of perfluorooctanoic acid (PFOA) and its detrimental environmental impacts have become a major focus of global attention. This study focused on the synthesis of bimetallic CoMn$_2$O$_4$ spinel by using the simple precipitation method followed by calcination at 550 °C. The peroxymonosulfate (PMS, HSO$_5^−$) activation efficiency of as-synthesized catalyst has been investigated for PFOA degradation in PMS activated CoMn$_2$O$_4$ catalytic system. Factors affecting the degradation efficiency were systematically examined. Under the optimal conditions (PMS concentration of 0.4 mM, catalyst dosage 0.2 g L$^{−1}$, and pH 5), the removal rate of PFOA (0.024 mM) was reached ∼ 90 % with a defluorination rate of 44 % after 180 mins at 30 °C. Bimetallic CoMn$_2$O$_4$ spinel oxide exhibited much better catalytic activity than single metal oxide of Mn and Co due to the formation of redox cycles between ≡Mn$^{2+}$/≡Mn$^{3+}$/≡Mn$^{4+}$ and ≡Co$^{3+}$/≡Co$^{2+}$ and their synergistic interaction between Mn and Co species confirmed by various characterization techniques. The radical scavenger tests and electron paramagnetic resonance (EPR) results testified that $^•$OH and SO$_4^{•−}$ were the main reactive oxidation species (ROS) for the stepwise removal of PFOA. Additionally, five experimental runs were performed to prove the higher stability, reusability and superb performance with extremely low metal leaching. A marginal reduction in the removal of used catalysts was detected during four cycles. Overall, unique structural features of CoMn$_2$O$_4$/PMS system confirmed the excellent catalytic performance in the remediation of emerging pollutants.

• Jezik: Angleški jezik
• Ključne besede: perfluorooctanoic acid, peroxymonosulfate, bimetallic cobalt manganate spinel, decomposition and defluorination, reusability and stability, degradation mechanism, PFOA, PMS
• Vrsta gradiva: Članek v reviji
• Tipologija: 1.01 - Izvirni znanstveni članek
• Organizacija: FKKT - Fakulteta za kemijo in kemijsko tehnologijo
• Status publikacije: Objavljeno
• Različica publikacije: Objavljena publikacija
• Leto izida: 2026
• Št. strani: 13 str.
• Številčenje: Vol. 321, pt. A, art. 122792
• PID: 20.500.12556/RUL-175291
• UDK: 546.7:544.478
• ISSN pri članku: 0009-2509
• DOI: 10.1016/j.ces.2025.122792
• COBISS.SI-ID: 254473219
• Datum objave v RUL: 23.10.2025

Gradivo je del revije

• Naslov: Chemical engineering science
• Skrajšan naslov: Chem. eng. sci.
• Založnik: Elsevier
• ISSN: 0009-2509
• COBISS.SI-ID: 838916

Licence

• Licenca: CC BY 4.0, Creative Commons Priznanje avtorstva 4.0 Mednarodna
• Povezava: http://creativecommons.org/licenses/by/4.0/deed.sl
• Opis: To je standardna licenca Creative Commons, ki daje uporabnikom največ možnosti za nadaljnjo uporabo dela, pri čemer morajo navesti avtorja.

Sekundarni jezik

• Jezik: Slovenski jezik
• Ključne besede: perfluorooktanojska kislina, PFOA, peroksimonosulfat, PMS, bimetalni kobaltov manganat spinel, razgradnja in defluoriranje, ponovna uporabnost in stabilnost, mehanizem razgradnje